The impact of chloride desalination on the corrosion rate of archaeological iron

Rimmer, Melanie, Watkinson, David ORCID: https://orcid.org/0000-0002-5696-9780 and Wang, Quanyu 2013. The impact of chloride desalination on the corrosion rate of archaeological iron. Studies in Conservation 58 (4) , pp. 326-337. 10.1179/2047058412Y.0000000068

Full text not available from this repository.

Abstract

Although desalination of archaeological iron reduces its chloride concentration and enhances object stability, the reduction in corrosion rate that this produces has never been quantified. This study measures post-treatment corrosion rates in accelerated corrosion environments to identify the impact of removing chloride ions on corrosion rate. Thirty-five archaeological iron nails, treated individually in either alkaline sulphite or nitrogen-deoxygenated sodium hydroxide, were exposed to 75°C and 75% relative humidity together with 31 untreated objects from the same archaeological sites. Object weight change and visual examination of physical change before and after the test period were used to monitor corrosion. 77% of treated objects showed no weight gain and no visible signs of corrosion, while 90% of untreated objects did corrode. The impact of chloride on corrosion of untreated objects was clearly established by a significant linear correlation between chloride content and weight gain. Treated objects with <400 ppm chloride content showed no corrosion behaviour. Corrosion of treated objects was attributed to incomplete treatment: 93% of objects treated to <5 mg/l Cl− in the final solution bath displayed no corrosion behaviour. Based on these results, desalination of iron objects to enhance their stability offers a valuable option for reducing corrosion rates of archaeological iron, which should increase object lifespan. The results also raise the question of whether low levels of post-treatment residual chloride produce corrosion of any significance. Answering this will be an important step forward for managing the preservation of archaeological iron.

Item Type: Article
Date Type: Publication
Status: Published
Schools: History, Archaeology and Religion
Subjects: C Auxiliary Sciences of History > CC Archaeology
Uncontrolled Keywords: Accelerated aging; Alkaline sulphite; Archaeological iron; Chloride; Corrosion rate; Desalination; Sodium hydroxide
Publisher: Earthscan
ISSN: 0039-3630
Funders: AHRC
Last Modified: 25 Oct 2022 08:23
URI: https://orca.cardiff.ac.uk/id/eprint/52614

Citation Data

Cited 17 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item Edit Item