Temperature dependence of magnetic anisotropy in Mn-substituted cobalt ferrite

Melikhov, Yevgen, Snyder, John Evan, Jiles, David C, Ring, A. P., Paulsen, J. A., Lo, C. C. H. and Dennis, K. W, 2006. Temperature dependence of magnetic anisotropy in Mn-substituted cobalt ferrite. Journal of Applied Physics 99 (8) , 08R102. 10.1063/1.2151793

[img]
Preview
PDF
Download (155kB) | Preview

Abstract

The temperature variation of magnetic anisotropy and coercive field of magnetoelastic manganese-substituted cobalt ferrites (CoMnxFe2?xO4 with 0 ? x ? 0.6) was investigated. Major magnetic hysteresis loops were measured for each sample at temperatures over the range 10–400 K, using a superconducting quantum interference device magnetometer. The high-field regimes of the hysteresis loops were modeled using the law of approach to saturation equation, based on the assumption that at sufficiently high field only rotational processes remain, with an additional forced magnetization term that was linear with applied field. The cubic anisotropy constant K1 was calculated from the fitting of the data to the theoretical equation. It was found that anisotropy increases substantially with decreasing temperature from 400 to 150 K, and decreases with increasing Mn content. Below 150 K, it appears that even under a maximum applied field of 5 T, the anisotropy of CoFe2O4 and CoMn0.2Fe1.8O4 is so high as to prevent complete approach to saturation, thereby making the use of the law of approach questionable in these cases.

Item Type: Article
Date Type: Publication
Status: Published
Schools: Engineering
Additional Information: ------- Publisher's copyright requirements "Copyright (2004) American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article appeared in Tian, Y and Li, G and Shinar, J and Wang, N. L. and Cook, B A and Anderegg, J. W. and Constant, A. P. and Russell, A M and Snyder, John Evan (2004) Electrical transport in amorphous semiconducting AlMgB14 films. Applied Physics Letters , 85 (7). pp. 1181-1183. ISSN 10773118 (10.1063/1.1781738)and may be found at http://apl.aip.org/resource/1/applab/v85/i7/p1181_s1."
Publisher: American Institute of Physics
ISSN: 1089-7550
Last Modified: 15 Dec 2017 08:37
URI: http://orca-mwe.cf.ac.uk/id/eprint/1923

Citation Data

Cited 61 times in Google Scholar. View in Google Scholar

Cited 110 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item Edit Item